Memoirs of the Literary and Philosophical Society of Manchester, Volume 11The Society, 1842 - Science |
From inside the book
Results 1-5 of 51
Page 182
... centre , after having sustained a load of 448 lbs . for 37 days . The deflection was observed to have increased from 1.904 to 2.014 between the time of loading and that of the last measurement , three days before the rupture took place ...
... centre , after having sustained a load of 448 lbs . for 37 days . The deflection was observed to have increased from 1.904 to 2.014 between the time of loading and that of the last measurement , three days before the rupture took place ...
Page 185
... centre . 476 1.700 broke Broke one inch from the centre . 896 .370.040 952 broke .. Ultimate deflection .399 . Broke at the centre . Results reduced to those of Bars 1.00 inch square . Specific Gravity Modulus of elasticity in lbs ...
... centre . 476 1.700 broke Broke one inch from the centre . 896 .370.040 952 broke .. Ultimate deflection .399 . Broke at the centre . Results reduced to those of Bars 1.00 inch square . Specific Gravity Modulus of elasticity in lbs ...
Page 186
... centre . - The from the centre . elasticity seemed to be injured with 30lbs or less- tion increased from .270 to .277 ; the defect of elasticity from .028 to 034 . Product Results reduced to those of bars 1.00 inch square. No. II . Load ...
... centre . - The from the centre . elasticity seemed to be injured with 30lbs or less- tion increased from .270 to .277 ; the defect of elasticity from .028 to 034 . Product Results reduced to those of bars 1.00 inch square. No. II . Load ...
Page 188
... centre . € 1,895 . Broke one inch from Broke of an inch from the centre . 434lbs . were hung from the bar for 14 ] hours , when the deflec- tion was found to be 1.630 , and the defect of lelasticity .292 . .. Ultimate deflection .493 ...
... centre . € 1,895 . Broke one inch from Broke of an inch from the centre . 434lbs . were hung from the bar for 14 ] hours , when the deflec- tion was found to be 1.630 , and the defect of lelasticity .292 . .. Ultimate deflection .493 ...
Page 190
... centre . Broke an inch from the centre when the Broke of an inch weight 1008 was re- from the centre , placed . 924 broke 1008 .379 .045 Ultimate deflection .384 . Deflection load removed . Experiment 1st , bar 4ft . 6in between ...
... centre . Broke an inch from the centre when the Broke of an inch weight 1008 was re- from the centre , placed . 924 broke 1008 .379 .045 Ultimate deflection .384 . Deflection load removed . Experiment 1st , bar 4ft . 6in between ...
Other editions - View all
Common terms and phrases
1.00 inch square anhydrous anthracite antimony appearance April arsenic atmosphere atom oil bar 4ft Bar 5 feet bars 1.00 inch Black bass Breadth Breaking Ultimate breaking weight Broke inch broke Ultimate deflection carbonate centre cities coal crystals Deflection in inches Deflection in Weight Deflection inches Deflection load removed Depth of bar diluted Distance between Distance Distance between supports elasticity in lbs ENGLISH IRONS Experiment 1st Experiment 3rd Experiment 4th grains of water Greek Henry Hobson Hot Blast hydrogen inch of mercury Interval January lbs Deflection lime water Lin and wool load removed Manchester ment mercury metal Mycenae observed oil of vitriol Pig Iron produced quantity resisting impact Results reduced Roman Soapstone Society Soft blue stone Specific Gravity specific heat specimens style sulphuric acid supports 2ft temperature tion tube Ultimate deflection vapour point Weight in lbs Weight of Bar WELSH IRONS White rock Ystalyfera